7/23/2019 Reporte Tecnico de Durezas
1/15
Reporte de durezas Rockwell y Brinell Equipo # 4
ENSAYOS DE DUREZA ROCKWELL
OBJETIVO:
Conocer el procedimiento normativo de los ensayos para comprobar
la dureza en el acero 9840. As como en los diferentes tipos de materiales
asignados a los dems equipos.
JUSTIFICACION:
Al determinar las propiedades mecnicas de los materiales nos
proporcionan datos que podemos utilizar para un diseo ms ptimo
referente a las propiedades conocidas mediante la informacin recabada en
los ensayos realizados.
En nuestro caso el acero AISI 9840, en el cual por diferentes pruebas
pudimos establecer su dureza.
Tambin podemos determinar por su dureza una comparativa con respecto
a su resistencia a la traccin por la ley de Dommer.
7/23/2019 Reporte Tecnico de Durezas
2/15
Reporte de durezas Rockwell y Brinell Equipo # 4
METODOLOGA:
Normas : ASTM A 370
Designation: A 370 03a
Standard Test Methods and Definitions for
Mechanical Testing of Steel Products1
This standard is issued under the fixed designation A 370; the number immediately following the
designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates
the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.
1These test methods and definitions are under the jurisdiction of ASTM Committee A01 on Steel,
Stainless Steel and Related Alloys and are the direct responsibili ty of
Subcommittee A01.13 on Mechanical and Chemical Testing and Processing Methods of Steel Products
and Processes.Current edition approved June 10, Oct. 1, 2003. Published July October 2003. Originally approved in
1953. Last previous edition approved in 20023 as A 370 02e1.
A 370 03.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1. Scope*1.1 These test methods2 cover procedures and definitions for the
mechanical testing of wrought and cast steels, stainless steels, and related
alloys. The various mechanical tests herein described are used to determineproperties required in the product specifications. Variations in testingmethods are to be avoided, and standard methods of t esting are to be
followed to obtain reproducible and comparable results. In those cases inwhich the testing requirements for certain products are unique or at
variance with these general procedures, the product specification testingrequirements shall control.
1.2 The following mechanical tests are described:Sections
Tension 5 to 13Bend 14Hardness 15Brinell 16Rockwell 17Portable 18Impact 19 to 28
7/23/2019 Reporte Tecnico de Durezas
3/15
Reporte de durezas Rockwell y Brinell Equipo # 4
Rockwell B
1er paso: Seleccionar el tipo de ensayo a realizar
2do paso: Ahora en el durmetro se selecciona la carga, la mesa de trabajo
o yunque y se coloca el Identador.
3er paso: Se coloca la pieza o probeta y aplicamos una precarga elevando
el husillo procurando que la aguja en la escala gire menos de tres cuartos de
vuelta de lo contrario el ensayo no es confiable.
4to paso: Accionamos la palanca de carga inicial la cual nos indicara los
giros de la aguja.
5to paso: Aplicamos con la palanca la carga total a la pieza o probeta
esperando a que el manmetro se detenga y nos indique la dureza en la
caratula.
Se realizaran tres identaciones y se promediaran, esto nos dar la dureza
que debemos compara en tablas de dureza.
EQUIPO UTILIZADO:
Durmetro para ensayo Rockwell.
ESPECIFICACIONES
Tres identadores:
-cono diamante a 120 escala A,C,D
-esfera de 1/16 escala B,F,G
-esfera de 1/8 escala E
Nueve escalas:
- A con 60 kg - B con 100 kg
- C con 150 kg - D con 100 kg
- E con 100 kg - F con 60 kg
- G con 150 kg
7/23/2019 Reporte Tecnico de Durezas
4/15
Reporte de durezas Rockwell y Brinell Equipo # 4
DATOS OBTENIDOS:
Ensayo ROCKWELL B, F, G, E
Indentador:
Esfera de acero f = 1/16(HRB, HRF, HRG)
Esfera de acero f = 1/8 (HRE)
Carga:
PB = 100 KgPF = 60 KgPG = 150 Kg
PE = 100 Kg
Formula: HRB, HRF, HRG, HRE = 130 -500t
Rockwell B:
Dimensiones de la Probeta : 2 de diametro por1/2 de espesorMaterial: Acero AISI 9840Penetrador: Esfera de 1/16precarga 2 1/2 vueltas = 10 kgCarga 100 kg
Huella # 13/4 de vuelta Lectura de 78
Huella # 23/4 de vuelta Lectura de 78
Huella # 33/4 de vuelta Lectura de 80
Se promedian las lecturas: (78 + 78 + 80)/ 3 = 78.6
7/23/2019 Reporte Tecnico de Durezas
5/15
Reporte de durezas Rockwell y Brinell Equipo # 4
Dureza Rockwell Interpolada con Brinell
DurezasDureza de Norma 201 HBN
Dureza tabulada 149 HBN
Dureza calculada 147.36 HBN
% de errores%E DN/ DT 25.87 %%E DN/ DC 26.68 %%E DT/ DC 1.10 %
Resistencia a la TensinRT Norma 103515 psi
RT Tabulada 76735 psi
RT Calculada 75890 psi
% de errores%E RN/ RT 25.87 %%E RN/ RC 26.68 %%E RT/ RC 1.10 %
7/23/2019 Reporte Tecnico de Durezas
6/15
Reporte de durezas Rockwell y Brinell Equipo # 4
ENSAYOS DE DUREZA BRINELL
OBJETIVO:
Conocer el procedimiento normativo de los ensayos para comprobar
la dureza en el acero 9840. As como en los diferentes tipos de materiales
asignados a los dems equipos.
JUSTIFICACION:
Al determinar las propiedades mecnicas de los materiales nos
proporcionan datos que podemos utilizar para un diseo ms ptimo
referente a las propiedades conocidas mediante la informacin recabada en
los ensayos realizados.
En nuestro caso el acero AISI 9840, en el cual por diferentes pruebas
pudimos establecer su dureza.
Tambin podemos determinar por su dureza una comparativa con respectoa su resistencia a la traccin por la ley de Dommer.
7/23/2019 Reporte Tecnico de Durezas
7/15
Reporte de durezas Rockwell y Brinell Equipo # 4
METODOLOGA:
Normas : ASTM A 370
Designation: A 370 03a
Standard Test Methods and Definitions for
Mechanical Testing of Steel Products1
This standard is issued under the fixed designation A 370; the number immediately following the
designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates
the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.
1These test methods and definitions are under the jurisdiction of ASTM Committee A01 on Steel,
Stainless Steel and Related Alloys and are the direct responsibility of
Subcommittee A01.13 on Mechanical and Chemical Testing and Processing Methods of Steel Products
and Processes.Current edition approved June 10, Oct. 1, 2003. Published July October 2003. Originally approved in
1953. Last previous edition approved in 20023 as A 370 02e1.
A 370 03.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.
1. Scope*1.1 These test methods2 cover procedures and definitions for the
mechanical testing of wrought and cast steels, stainless steels , and related
alloys. The various mechanical tests herein described are used to determineproperties required in the product specifications. Variations in testingmethods are to be avoided, and standard methods of testing are to be
followed to obtain reproducible and comparable results. In those cases inwhich the testing requirements for certain products are unique or at
variance with these general procedures, the product specification testingrequirements shall control.
1.2 The following mechanical tests are described:Sections
Tension 5 to 13Bend 14Hardness 15Brinell 16Rockwell 17Portable 18Impact 19 to 28
7/23/2019 Reporte Tecnico de Durezas
8/15
Reporte de durezas Rockwell y Brinell Equipo # 4
Brinell Normal
1.- Seleccionar el material "que en la industria es muestreo de material"
2.- verificar que no tenga defectos superficiales, como golpes, enterraduras
de herramienta (ralladuras de la probeta), oxidaciones, corrosiones, grasaso aceites.
3.- seleccionar la carga, penetrador y tiempo.
4.- montaje del penetrador en el husillo porta herramientas.
5.- montaje de la escala o rango de cargas en la caratula de la maquina.
6.- colocar el pndulo en el orificio correspondiente a la escala
seleccionada con el contrapeso o sin el contrapeso)
7.- seleccionar la mesa adecuada segn la forma de la pieza.
8.- montar la probeta en la mesa de trabajo o yunque.
9.- formar la cmara hidrulica o colchn de aceite con un peso de 50 kg de
inicio.
a.- verificar que la vlvula de descarga este abierta y la de carga cerrada.
b.- poner a trabajar el motor y cerrar la vlvula de descarga.
c.- abrir la vlvula de carga hasta que el embolo se eleve un centmetro
aproximadamente y se presente un ligero contacto. una vez transcurrido el
centmetro, cerrar la vlvula de carga.
d.- verificar que la manecilla primaria este en cero, sino estuviera en cero
se tiene que ajustar con el tornillo y tuerca de nivelacin.
10.- comenzar el ensayo haciendo contacto el penetrador con la pieza y
aplicar una carga inicial de 10 kg a 15 kg.
11.- abrir la vlvula de carga durante 10 o 15 segundos si el material es
duro, si el material es suave se mantiene de 30 segundos a 3 minutos.
12.- abrir la vlvula de descarga.
13.- extraer la pieza o probeta y medir el dimetro de la huella con el
microscopio de taller.
7/23/2019 Reporte Tecnico de Durezas
9/15
Reporte de durezas Rockwell y Brinell Equipo # 4
14.- calcular la dureza por formula-
15.- determinar la dureza tubularmente.
16.- verificar el porcentaje de error.
17.- determinar el tipo de material en las tablas.
Nota: para Brinell especial es el mismo procedimiento.
EQUIPO UTILIZADO:
y Prensa hidrulica Universal
Marca: AMSLER
Caractersticas :
Manmetro de pndulo de longitud y masa variable que maneja dos tipos
de ensayo
1.- Brinell especial de 3000kg a 5000kg con contrapeso
2.- Brinell normal de 500kg a 1000kg sin contrapeso
El contrapeso es de 18kg
Electrohidrulica
Partes principales:
Chasis o carcasa
Motor y motobomba
recipiente para aceite
tubo de descarga de dimetro mayor
tubo de carga de dimetro menor
7/23/2019 Reporte Tecnico de Durezas
10/15
Repo
te de du
ezas Ro
ell y B
inellquipo#4
Embolo secundario
tirante
excntrica Dinammetro
flecha
Tornillo y tuerca de ajuste a un costado del pndulo
Caratula de la maquina con dos manecillas:
Negra :indica el cero sin carga
Roja :indica la carga aplicada al material
Volante elevador de husillo
husillo porta herramientas
mesa de trabajo o yunque para probeta cilndrica con asiento de rotula
arandela de fijacin de la rotulapista de la rotula
palanca selectora de mbolos.
y Microscopio de taller.
Datos obteni os
Ensayo INE .
Indentador: E
f
Carga
P
Frm la:HBN
7/23/2019 Reporte Tecnico de Durezas
11/15
Reporte de durezas Rockwell y Brinell Equipo # 4
Brinell normal:
Penetrador: Esfera de 10 mmPrecarga: 10 kgTiempo: 15 s
Escala: 5000 kgCarga: 1500 kgDimetro de huella: 4.9Dureza tabulada: 149Dureza calculada x formula: 148,88% de error: 0.080
Para Brinell Normal
DurezasDureza de Norma 201 HBN
Dureza tabulada 149 HBN
Dureza calculada 148.88 HBN
% de errores%E DN/ DT 25.87 %%E DN/ DC 25.93 %%E DT/ DC 0.08 %
Resistencia a la TensinRT Norma 103515 psi
RT Tabulada 76735 psi
RT Calculada 76673 psi
% de errores%E RN/ RT 25.87 %%E RN/ RC 25.93 %
%E RT/ RC 0.08 %
7/23/2019 Reporte Tecnico de Durezas
12/15
Reporte de durezas Rockwell y Brinell Equipo # 4
Brinell especial:
Penetrador : Esfera de 5 mmPrecarga : 10 kgTiempo: 15 s
Escala en durmetro : 3000 kgCarga ( 30D2) : 750 kgDimetro de huella: 2.35Dureza tabulada: 165.0Dureza calculada x formula: 162.77% de error: 1.35
Para Brinell Normal
DurezasDureza de Norma 201 HBN
Dureza tabulada 165 HBN
Dureza calculada 162.77 HBN
% de errores%E DN/ DT 17.91 %%E DN/ DC 19.01 %
%E DT/ DC 1.35 %
Resistencia a la TensinRT Norma 103515 psi
RT Tabulada 76735 psi
RT Calculada 76673 psi
% de errores
%E RN/ RT 17.91 %%E RN/ RC 19.01 %%E RT/ RC 1.35 %
7/23/2019 Reporte Tecnico de Durezas
13/15
Reporte de durezas Rockwell y Brinell Equipo # 4
CONCLUCIONES TECNICAS.
Luis Alberto Maya Aguilar
Se puede apreciar que las caractersticas de los materiales es
determinable mediante los ensayos con los que estudiamos suspropiedades, afortunadamente pudimos corroborar que los
procedimientos como las maquinas generaron datos mnimamente debajo
de los resultados tabulados, es decir las maquinas del laboratorio siguen
brindando con un uso adecuado, datos confiables. Cabe decir que la
variacin tambin pudo ser causada por una probeta defectuosa y otros
factores difcilmente determinables.
7/23/2019 Reporte Tecnico de Durezas
14/15
Reporte de durezas Rockwell y Brinell Equipo # 4
COTIZACION.
7/23/2019 Reporte Tecnico de Durezas
15/15
Reporte de durezas Rockwell y Brinell Equipo # 4
Fuentes de Informacin
Tablas de dureza del Laboratorio de ciencias.
Para las imgenes de las pruebas.
http://www2.ing.puc.cl/~icm2312/apuntes/materiales/materials6-2.html
Para las normas:
Catalogo de normas ASTM
Catalogo de normas de la SECOFI
Recommended